Electrical conductivity of nanocrystalline ceria and zirconia thin films
The results of studies of the preparation, structure and electrical conductivity of ZrO2:16% Y and CeO2 thin films are presented. Dense films with grain size controlled in the region of 1–400 nm have been obtained on monocrystalline sapphire and polycrystalline Al2O3 substrates using a polymeric precursor spin coating method. The electrical conductivity of nanocrystalline thin [...]
Dissertation of G. Zhou (University of Pennsylvania, 2008)
«Characterization of the equilibrium redox properties for ceria-based mixed oxides»
Abstract/summary is available at ProQuest site
Методом кулонометрического титрования исследованы окислительно-восстановительные свойства высокодисперсного диоксида церия, а также твердых растворов и композитов на его основе, включая CeO2/Al2O3, Ce1-xZrO2, Ce1-xTiO2, Ce1-xHfO2, Ce1-xMnO2, Ce1-xTbO2. Изучены каталитические свойства полученных твердых растворов.
Dissertation of M.A. Panhans (Marquette University, 1990)
«A thermodynamic and electrical conductivity study of nonstoichiometric cerium dioxide»
Abstract/summary is available at ProQuest site
Проведены исследования электропроводности моно- и поликристаллического нестехиометричного диоксида церия в области, соответствующей переходу от n- к p-типу проводимости (800оС). Методом кулонометрического титрования при указанной температуре установлено, что подвижность электронов существенно превосходит подвижность дырок.